Synthene FASTElast 35 A POLYOL

The Synthene Fast-Elast system is a polyurethane elastomer system (type rubber / rubber) developed for the manufacture of technical parts and flexible prototypes. Composed of three components, it allows you to simply obtain a broad spectrum of hardness ranging from 35ShA (very flexible) to 93 ShA (semi rigid), while offering very good mechanical performance.

Fast-Elast 35 A POLYOL : Color : Clear / Viscosité 350 - Mix Système : Synthene Fast-Elast : Color: Amber / Viscosity : from 300 to 350 mPa.s / color : clear to white / Maximum thickness : from 20mm to 30 mm depend of hardness / Reactivity (200gr): 6 to 12min / Hardness : from 35 ShA to 93ShA / Elongation at break : from 350% to 1110% (TDS) / Tear resistance : from 7,8 to 60 kN.m¯¹ (TDS).

The Synthene Fast-Elast System allows a very short demolding time (1 hour at 70 ° C) with a very low viscosity (between 300 and 350 mPa.s) allowing easy filling of the molds, even for very fine parts. It is stainable, and offers excellent mechanical performance: excellent elongation and very good tear behavior (even with primer). Fast-Elast 93A Polyol can be mixed with Fast-Elast 93A Polyol and Fast-Elast 35-93A Isocyanate to obtain the desired hardness (see ratios on the technical sheet)